In order to further transform the operation mechanism, establish the operation concept of "market-oriented, customer-centric", strive to improve our core competitiveness and promote the rapid development of business; further strengthen customer marketing management, subdivide customer groups, establish a top-down, crisscross, hierarchical marketing mechanism of "everyone is a marketer", and provide for the needs of different levels of customers Corresponding services.
The hot rolling method is to heat the SA283 Gr.C, S235JR, S355 mild steel steel material to about 1000 ℃ ~ 1250 ℃ and use the rolling mill to roll it. The traditional hot rolling process is generally divided into the following two steps: the first step is to use the primary rolling mill or billet rolling mill to roll the ingot, billet or continuous casting billet into a certain shape and size of billet. This kind of SA283 Gr.C, S235JR, S355 mild steel rolling process is usually called semi-finished product production, also called blank production.
Asme sa514 grade B quenched and tempered alloy steel element composition%C: 0.12-0.21, Si: 0.20-0.35, Mn: 0.70-1.00, P max.: 0.035, S max.: 0.035, B max.: 0.005, Cr: 0.40-0.65, Mo: 0.15-0.25, V: 0.03-0.08, Ti: 0.01-0.03The mechanical properties in thickness (mm)T≤65Yield strength (≥Mpa): 690Tensile strength (Mpa):760-895Elongation in ≥,%: 18
Since its inception, the company has always adhered to the development policy of "survival with quality, development with products, cooperation with credibility, and service with customers". I would like to express my heartfelt thanks to the old and new friends and customers who have always given care, support and help to the company! And sincerely hope to establish a long-term cooperative relationship with them, mutual benefit and common development.