A514 gr M alloy structural steel chemical composition (melting analysis)%C: 0.12-0.21, Si: 0.20-0.35, Mn: 0.45-0.70, P max.: 0.035, S max.: 0.035, Ni: 1.20-1.50, Mo: 0.45-0.6.0, B: 0.001-0.005The mechanical properties in thickness (mm)T≤65Yield strength (≥Mpa): 690Tensile strength (Mpa):760-895Elongation in ≥, %: 18
The company's ESP thin gauge is down to 0.6mm. The thinner the thickness of the A537 Class 2 strucutural carbon steel, hot rolled steel product, the more difficult it is to roll. The thickness will encounter increased load, severe vibration of the rolling mill, difficult shape control, and fluttering of the head during the downdraft. There are many problems such as difficulty in getting bite, which limit the thinnest size that can be rolled by hot rolling. At present, the thinnest gauge of conventional rolling line is 1.2mm, and the thinnest gauge of CSP production line is about 1.0mm. The successful rolling of 0.6mm hot rolled steel product is a milestone in hot rolled steel strip technology.
Compared with the traditional seamless steel pipe, alloy seamless pipe has better performance in all aspects. Because of the addition of various metal elements in the manufacturing, the overall strength of the alloy seamless pipe is larger, stronger and durable, and the service performance and service life of the A537 Class 2 strucutural carbon steel, alloy seamless pipe are improved. The alloy seamless pipe is the best choice especially for special environment and high pressure requirements. Because of its high material properties, alloy seamless pipe has good corrosion resistance. It is not easy to be corroded in some special environment, which reduces the cost of the project and has a longer service life.