ASTM A537 steel is a heat-treated carbon silicon manganese steel plate for ASTM pressure vessels, which is divided into 3 levels A537 CL1, A537 CL2, A537 CL3. SA515Gr65 asme carbon steel sheet, A537 CL1 plates delivery status: normalizing; When the A537 CL1 plate thickness is ≤65mm, the yield strength is ≥345MPa, and the tensile strength is ≥485MPa. When the thickness is 65 - 100mm, the yield strength is ≥310MPa and the tensile strength is ≥450MPa.
In order to prevent the deformation of SA515Gr65 asme carbon steel sheet, wear-resistant composite plate during preheating, the steel plate with good quality should be selected first. The steel plate with serious carbide segregation should be reasonably cast and heat treated by quenching and tempering. For the large and non cast wear-resistant composite plate, the solution double refining heat treatment can be carried out. At the same time, the heating temperature should be reasonably selected and the heating speed should be controlled.
Preheating cutting: The most effective way to prevent steel plate cutting cracks is to preheat before cutting. Before flame cutting, the steel plate is usually preheated, and the preheating temperature mainly depends on the quality level and thickness of the steel plate. The preheating method can be carried out with flame burner, electronic heating pad, or heating furnace. In order to determine the preheating effect of the steel plate, the required temperature should be tested at the heating point.
We should help solve the customer's problems in time, not just verbally, without solving the problems or shirking the responsibility. Improving after-sales efficiency can make customers feel respect. We should take their problems seriously and show sincerity. It can also give customers a good impression and reduce the negative impact.