Titanium microalloying is an element of plate sa283 and 1008 steel strengthening complex with carbon and nitrogen. The addition of micro amount of titanium in the steel can fix almost all nitrogen and part carbon in the steel, so as to eliminate the strain aging phenomenon and improve the aging impact performance of the steel. At the same time, it can refine the grains and change the morphology of the compounds. According to the atomic weight ratio of Ti and N in plate sa283 and 1008 steel tin formula (Ti = 3.4n), the content of Ti in steel should be controlled between 0.015 and 0.025%. Generally, the amount of ferrotitanium added to each ton of steel is 1kg.
asme sa514 gr.P quenched and tempered alloy steel element composition%
C: 0.12-0.21, Si: 0.20-0.35, Mn: 0.45-0.70, P max.: 0.035, S max.: 0.035, Ni: 1.20-1.50, Cr: 0.85-1.20, Mo: 0.45-0.6.0, B: 0.001-0.005
The mechanical properties in thickness (mm)T≤65
Yield strength (≥Mpa): 690
Tensile strength (Mpa):760-895
Elongation in ≥,%: 18
The company operates on the principles of fairness, objectivity, science, pragmatism and integrity. The management treats people with courtesy, takes sincerity as the standard management, dares to open up, unites and advances, carries on the past and makes unremitting efforts, seizes the good trend of economic development, strengthens exchanges with peers, makes friends with all walks of life, keeps pace with the times and creates greater brilliance of the enterprise, and makes its own contribution to the prosperity and development of the steel industry.